HARDFACE HC-O x 1.6mm
CLASSIFICATION
EN 14700 T Fe15
DESCRIPTION
• A flux cored/gasless, high chromium cast iron wire for hardsurfacing components subject to extremely severe abrasive wear and moderate impact
• The deposit contains a high proportion of hard primary chromium carbides in a tough austenitic matrix
APPLICATIONS
Hardface HC-O is used for hardfacing components subject to wear by earth, sand and abrasives.
Examples
Gyratory crusher cones and mantles, catalyst pipes and valves, slurry pipes and valve bodies, dredge pump bodies, sand dredge parts, extruder screws, “barmac” crushers, mining and earthmoving equipment, blast furnace bells, brick muller tyres, sugar mill crusher hammers, drag line components, coal pulverisor rolls, coke hammers, cone knives and shredders. Relief checking is normal and best limited to two layers unless impact loading is small. Can be multi-layered in specific applications.
TYPICAL ALL-WELD METAL ANALYSIS
C Mn Si Cr Fe
5.00 1.50 1.50 27.0 Rest
Structure: primary carbides and eutectic carbides of the M7C3 type in an austenitic matrix
TYPICAL ALL-WELD METAL MECHANICAL PROPERTIES
Hardness – 3-Layer deposit on mild steel: 60-62 HRc
CONDITIONS OF USE
Current type Shielding
DC (+) Self shielded
OPERATING CONDITIONS
Diameter Amperage [A] Voltage [V] Stick-out [mm]
[mm] Range Optimum Range Optimum Range Optimum
1.2 100 – 300 250 21 – 35 28 12 – 25 20
1.6 150 – 300 270 24 – 35 28 15 – 25 25
2.0 200 – 400 300 26 – 35 28 20 – 50 30
2.4 250 – 450 350 26 – 35 28 25 – 50 40
Recovery: 90%
WELDING POSITIONS
Flat, half up, half down
STANDARD DIAMETERS (mm)
1.2, 1.6, 2.0, 2.4,
REEL WEIGHT
15Kg